JF660镍锌烧结铁氧体片设计用WPC接收端,超薄设计,最薄可以最低0.065mm,性能稳定,低磁损,可替代市面上常用纳米晶材料,为客户研发设计提供完美的解决方案。
WPC无线充电模组
A4WP& WPC &NFC 三合一无线充电模组
Material characteristic
高磁导率,低磁损
超薄工艺,不受空间限制
柔性薄片,易于加工
环保无卤配方
性能:
Part No. |
JF660-xxx |
||
Effective carrier frequency |
100KB Hz ~ 13.56MHz |
||
Permeability (@ 100KHz) |
μ` |
660 ±15% |
|
μ`` |
10 (≤15) |
||
Saturation magnetic flux density |
BS |
25℃ |
390 |
60℃ |
350 |
||
Operating temperature |
-40(℃) to +85(℃) |
||
Dimensions (mm) |
115*125mm |
结构规格:
Part No. |
Size |
Total thickness |
Ferrite |
Cover Film |
Adhesive |
JF660-Z-P0005-F005-PS001 |
93*125mm |
0.065mm(±0.01mm) |
0.05mm |
0.01mm |
0.01mm |
JF660-Z-P001-F006-PS001 |
93*125mm |
0.08mm(±0.01mm) |
0.06mm |
0.01mm |
0.01mm |
JF660-Z-P001-F008-PS001 |
115*125mm |
0.1mm(±0.01mm) |
0.08mm |
0.01mm |
0.01mm |
JF660-Z-P001-F011-PS001 |
115*125mm |
0.13mm(±0.02mm) |
0.11mm |
0.01mm |
0.01mm |
JF660-Z-P003-F015-PS003 |
115*125mm |
0.21mm(±0.02mm) |
0.15mm |
0.03mm |
0.03mm |
JF660-Z-P003-F020-PS003 |
115*125mm |
0.26mm(±0.03mm) |
0.2mm |
0.03mm |
0.03mm |
JF660-Z-P003-F025-PS003 |
115*125mm |
0.31mm(±0.03mm) |
0.25mm |
0.03mm |
0.03mm |
JF660-Z-P003-F030-PS002 |
115*125mm |
0.36mm(±0.04mm) |
0.3mm |
0.03mm |
0.03mm |